We know that the main rubber component a of the insulating glass two-component rubber itself is not cured. It will be gradually cured only after a certain amount of curing agent is added. In order to appropriately speed up the curing speed of the rubber, we add a certain amount of curing accelerator to the curing agent to speed up the reaction speed between the curing agent and the main rubber.

当我们人为地为了加速胶的固化而加大固化剂用量比例时,胶虽然提高了硫化的速度但胶的本身质量却降低了,我们用刀片破开经加速硫化而固化的胶发现,这时的胶要比正常的胶松软的多,像发泡的海绵.故我们的工人在调配双组份胶时为了尽可能的保证胶的质量,一定要按标准的比例并充分混均以防止胶局部促进剂含量偏高从而影响中空玻璃的整体质量.

When we artificially increase the proportion of curing agent in order to accelerate the curing of rubber, although the curing speed of rubber is improved, the quality of rubber itself is reduced. We use a blade to break the rubber cured by accelerated curing. It is found that the rubber at this time is much softer than the normal rubber, like a foaming sponge. Therefore, in order to ensure the quality of rubber as much as possible when preparing two-component rubber, It must be fully mixed according to the standard proportion to prevent the high content of local accelerator from affecting the overall quality of insulating glass

中空玻璃双组份胶所用的原料，都具有很强的粘结力，但不管粘结力多强的材料其特性都需要特定的符合性能要求的条件下才能实现，我们所用的双组份胶它的*佳粘结力的产生(跟玻璃及铝条)是在其加入规定量固化剂后立即涂在所需涂布的部位让其在所涂布的部位完成从开始硫化———完全硫化的一个过程，如果我们将胶在半硫化状态下在涂所需部位，则粘结强度就大有影响。

The raw materials used in the two-component adhesive for insulating glass have strong adhesion, but no matter how strong the adhesion is, its characteristics can only be realized under specific conditions that meet the performance requirements, For the two-component adhesive we use, its * good adhesion (with glass and aluminum strip) is coated on the required coating part immediately after adding the specified amount of curing agent, so that it can complete the process from vulcanization to complete vulcanization at the coated part. If we apply the adhesive to the required part in the semi vulcanized state, the bonding strength will be greatly affected.